Ceramic-Coating HE
• for the coating of ceramics and metals
• good chemical stability
• high hardness and small porosity
• good adhesion on substrates
• for the high temperature application up to 1100°C (2013°F)

Description

Ceramic-Coating HE is a special coating on the basis of aluminium silicate. It shows a high hardness and is extremly resistant to abrasion. Due to the low porosity its permeability of gas is very small. Ceramic-Coating HE is prefereably used as protection and interface for metals and ceramics. Metals are for example protected with this product in order to prevent chemical attacks and other modifications at high temperatures. So the decarburisation of steel or the oxidation of nitrides are prevented. The substrates to be coated should indicate thermal coefficients of expansion of >8.5·10-6/K. For substrates with substantially smaller thermal coefficients of expansion the product Ceramic-Coating LE on the basis of stabilized zirconium oxide is available.

Application

• Resuspend Ceramic-Coating HE prior to use. Dilute with distilled water if necessary.
• Application on clean surfaces is possible by brushing, dipping or spraying.
• Dry thoroughly. Do not contact wet coatings with metal melts. Additional layers may be applied after drying.
• Curing of the coating should take place with 350 to 400°C (662-752°F).
• A thin coating application (50-100µm) is favourable. Thick layers may crack during use and tend to chip off.
• Tools can be cleaned with water.

Storage-Container Size

Containers should be kept closed and product protected against frost. A storage temperature of >5°C (>41°F) is recommended. Ceramic-Coating HE is available in 1kg-containers.

Safety Advices

Ceramic-Coating HE contains water, is solvent-free and according to data available to us a non-hazardous preparation. This product is alkaline and therefore labelled irritant. The use of eye and hand protection is recommended. An EC material safety data sheet is available.

Technical Data

Colour

yellow

Ceramic Constituent

Aluminium silicate

Binder

Alkali silicate

Composition

70%Al2O3 · SiO2

30% Alkali silicate

Solid Content

>53%

Density

>1.5 g/cm³

pH

11-12

Thermal expansion

>8.5·10-6/K

Temperature (max. Application)

1100°C (2013°F)

 


© 2015 Büro für angewandte Mineralogie · Dr. Stephan Rudolph · D-47918 Tönisvorst


These recommendations are believed to be correct. However, no guarantee of their accuracy is given. Therefore, purchasers shall make their own tests to determine suitability for their use. These products are offered for industrial and related uses (e.g. research and development) only. However the user must take the necessary precautions appropriate for products containing chemicals. This description does not imply the absence of any patents, the responsibility whatsoever solely rests with the user.